cuppy wire

用法例句

Cause analysis and control measures of longitudinal cracks on the surface of continuous casting slabs;

连铸板坯表面纵裂纹原因分析及控制措施

Controll the longitudinal crack of thin slab;

薄板坯连铸纵裂纹的控制

The pattern of the longitudinal cracks on surface of continuous casting slab was summarized.

综述了连铸板坯表面纵裂纹的形貌,分析了纵裂的形成机理及影响纵裂的各种因素,为采取措施减轻和避免这种质量缺陷提供依据。

This paper analyses the longitudinal crack on the near net shape beam blank web surface in Laigang, gives the influencing factors and improved measures.

对近终形异型坯腹板表面纵向裂纹问题进行了分析,找出了工艺和设备方面的影响因素,通过对钢水质量、冷却条件、设备结构等方面进行优化改进,解决了铸坯表面裂纹缺陷问题,铸坯质量合格率由94%提高到99。

The longitudinal crack of steel bar is the main factor that influences its quality.

钢棒的纵向裂纹是影响其质量的主要因素。

The longitudinal surface crack on thin slab is a serious quality defect at thin slab continuous casting and rolling process.

分析了薄板坯表面纵裂的成因;总结了薄板坯表面纵裂的特征、影响因素及其防止纵裂的措施;提出了今后研究纵裂纹的方向。

Study On Longitudinal Surface Cracks On CSP Hot-Rolled Plate

酒钢CSP热轧板卷表面纵裂纹研究

CAUSE ANALYSIS FOR SURFACE LONGITUDINAL CRACKS ON Q235B SLAB

Q235B钢板坯表面纵裂纹的原因分析

Improvement Practice of Reducing Surface Longitudinal Crack of Wide and Thick Slab

减少宽厚板坯表面纵裂纹的改进实践

Analysis and study of surface longitudinal cracks for SS400 steel sheet

SS400钢板表面纵裂纹分析及实验研究

Formation and prevention of grade 20 steel CC bloom surface longitudinal cracking

20钢φ180连铸坯表面纵裂纹的形成与防止

Technics Study of Reducing Longitudinal Surface Crack of Beam Blank

减少连铸异型坯表面纵裂纹的工艺研究

Synopsis This paper analyzes the reasons of forming longitudinal corner cracks for continuous casting billet of electric arc furnace and puts forward corresponding precaution measures.

通过分析电炉连铸坯产生角部纵裂纹的原因,提出了具体的控制措施。

MICROSEGREGATION OF SOLUTE ELEMENTS IN SOLIDIFYING MUSHY ZONE OF STEEL AND ITS EFFECT ON LONGITUDINAL SURFACE CRACKS OF CONTINUOUS CASTING STRAND

钢凝固两相区溶质元素的微观偏析及其对连铸坯表面纵裂纹的影响

Listed in Column 2 are descriptions of the cracking.

第二纵列是关于裂纹的描述。

Study on Corner Sink and Vertical Cracks of CC Steel Billet

连铸坯角部凹陷及纵向裂纹的研究

Longitudinal-cracking Failure Analysis of Box

φ139.7mm钻杆内螺纹接头纵向开裂失效分析

Research on Magnetic Testing Methods and Their Application to Longitudinal Cracks of Steel Bars;

钢棒纵向裂纹磁性检测方法及应用研究

Cause Analysis and Prevention Measure of Terminal Crack of Submerge-arc Welding Longtitudinal Weld

埋弧焊纵焊缝终端裂纹原因分析及预防措施

Generation Reason Analysis of Cold Crack in Welding Joint of Automobile Variable Speed Control Handle

汽车变速操纵杆焊接接头冷裂纹产生原因分析

Analysis on the tendency of welding hot cracks of aluminum alloy increased by longitudinal pre-tension

纵向预拉伸增大铝合金焊接热裂纹倾向的分析

The cracks are primarily parallel to the longitudinal direction of the girder and to the nominal bending stresses.

裂纹基本上平行于主梁纵向，既平行于名义弯曲应力。

This indicated that the fracture had initiated at the unfused butt weld in the longitudinal stiffener.

研究表明裂纹是从纵向加劲助未熔透的对接焊缝中起始的。